Description
Halogen-free fire retardant heat shrinkable tubing, made of radiation cross-linked polyolefin, is designed with excellent physicochemical and electrical properties. Typical applications include insulation of electrical connections or wire splices, rust and corrosion resistance for the soldered joints or connections, mechanical and wiring harness protection and insulation in electronics, communications, automotive, marine, aircraft manufacturing and other fields.
��?Features
��?Meets UL 224, CAN / CSA C22.2 NO198.1 -99
��?Heat shrink ratio : 2:1
��?Halogen-free , low-smoke generations , non-toxic , flexible , fire retardant
��?Min. shrink temperature : 84 ��?
��?Min. full recovery temperature :120 ��?
��?Continuous operating temperature : -55 ��?~ 125 ��?
��?Environmental standards : RoHS , IPC/JEDEC-J-STD-709 Class H material
��?Standard colors: black, white, red , yellow ,
Green, blue and other four international standard
colors. More colors are available upon request.
��?Technical Data
Properties Typical Data Test Method
Tensile strength（MPa��?��?0.4 ASTM D2671
Elongation��?��?��?00 ASTM D2671
Tensile strength after heat aging(***) ��?.3 158℃�?68h
Elongation after heat aging(%) ��?00 158℃�?68h
Longitudinal change(%) -5%��?5% ASTM D 2671
Flammability VW-1 ASTM D 2671 C
Voltage withstand(Rated voltage 600V) 2500V,1min, without breakdown UL224
Heat shock No cracking, no dripping UL 224��?50℃�?h
Dielectric strength ��?5kv/mm ASTM D 149
Volume resistivity(Ω cm) ��?014Ω.cm IEC 60093
��?Structure
��?Dimension
Size
Expanded
Internal diameter(mm) Recovered(mm) Standard Package
m/spool
Internal diameter Max(mm) Wall thickness（Min��?
φ0.5/0.35 0.7±0.2 ��?.35 0.33±0.10 400
φ0.6/0.40 0.9±0.2 ��?.40 0.33±0.10 400
φ0.8/0.50 1.1±0.2 �� |
| Company: |
Suzhou Volsun Electronics Technology Co., Ltd
|
| Contact: |
Ms. Carol gan |
| Address: |
NO.413 Mudong Road,Mudu Town,Wuzhong District,Suzhou City |
| Postcode: |
215101 |
| Tel: |
86-0512-66386909 |
| Fax: |
86-512-66386908 |
| E-mail: |
|
|
|
|
Home